Introducing high-quality Rubbers – meticulously produced through advanced manufacturing techniques, offering exceptional elasticity and durability. Ideal for a wide range of applications, including automotive components, industrial seals, footwear, and countless other products. Experience superior performance and reliability with our premium Rubbers
Accordion
Fuel & Energy
Petro Chemicals
Agri-Chemical & Organic Solutions
Minerals
HALOBUTYL RUBBER
Introducing Halobutyl rubber – a premium synthetic rubber renowned for its exceptional impermeability to gases and liquids. Produced through advanced halogenation techniques, it finds applications in tire inner liners, pharmaceutical stoppers, and various industries requiring superior barrier properties. Trust our Halobutyl rubber for unmatched performance and reliability.
Accordion
1. Bromobutyl Rubber
Introducing Bromobutyl rubber – a high-performance synthetic rubber produced through bromination techniques, ensuring excellent heat resistance and low permeability. Widely used in pharmaceutical closures, automotive parts, and various industrial applications. Experience the exceptional quality and versatility of Bromobutyl rubber for your needs.
1.1 Bromobutyl rubber BBK-232
It is a bromination product of butyl rubber with an unsaturation of at least 1.5 mol%.
| Mooney viscosity | 28 - 35 |
| Technical specification DS | TS 20.17.10-096-05766801-2017 |
| Shelf life | 1 year |
1.2 Bromobutyl rubber BIIR-232 plastic 0,54
It is a bromination product of butyl rubber with an unsaturation of at least 1.5 mol%.
| Packaging | Plastic container |
| Mooney viscosity | 28 - 35 |
| Technical specification DS | TS 20.17.10-096-05766801-2017 |
| Shelf life | 1 year |
2. Chlorobutyl Rubber
Introducing Chlorobutyl rubber – a top-grade synthetic rubber produced through chlorination techniques, offering superior ozone resistance and low gas permeability. Trusted in applications such as pharmaceutical stoppers, hoses, and industrial seals. Choose Chlorobutyl rubber for reliable performance and exceptional quality.
2.1 Chlorobutyl rubber CIIR-139
It is a product of chlorination of butyl rubber with an unsaturation of at least 1.8 mol%.
| Mooney viscosity | 45-55 |
| Technical specification DS | TS 20.17.10-096-05766801-2017 |
| Shelf life | 2 year |
2.2 Chlorobutyl rubber CIIR-139 plastic 0,54
It is a product of chlorination of butyl rubber with an unsaturation of at least 1.8 mol%.
| Packaging | Plastic container |
| Mooney viscosity | 45-55 |
| Technical specification DS | TS 20.17.10-096-05766801-2017 |
| Shelf life | 1 year |
POLYBUTADIENE RUBBER (BR)
Introducing Polybutadiene rubber (BR) – a versatile synthetic rubber produced through polymerization, known for its excellent resilience, low heat build-up, and high tear strength. Widely used in tire manufacturing, industrial goods, and various engineering applications. Experience the exceptional performance of Polybutadiene rubber for your specific needs.
1. BR-Li
Introducing Polybutadiene rubber (BR-Li) – an advanced synthetic rubber produced by incorporating lithium as a catalyst, resulting in enhanced elasticity and improved processability. It finds applications in high-performance tires, automotive components, and specialized industrial products. Trust the superior quality of BR-Li for your demanding applications.
1.1 Rubber BR-4170 plastic 0,54
Solution polymerization product of butadiene in the presence of an organolithium catalyst.
| Packaging | Plastic container |
| Mooney viscosity | 45-65 |
| Technical specification DS | TS 20.17.10-140-05766801-2021 |
| Shelf life | 1 year |
2. BR-Nd
Introducing Polybutadiene rubber (BR-Nd) – a premium synthetic rubber produced by incorporating neodymium as a catalyst, resulting in exceptional tensile strength, abrasion resistance, and heat stability. Ideal for demanding applications such as conveyor belts, mechanical goods, and high-performance automotive parts. Choose BR-Nd for superior performance and durability.
2.1 Rubber BR-544NP plastic 0,54
Synthetic butadiene rubber SKD-544NP is a product of butadiene polymerization in an aliphatic hydrocarbon medium in the presence of a catalytic system based on neodymium compounds
| Packaging | Plastic container |
| Mooney viscosity | 40-49 |
| Technical specification DS | TS 20.17.10-100-05766801-2021 |
| Shelf life | 2 year |
2.2 Rubber BR-563 plastic 0,54
Synthetic butadiene rubber SKD-563 is a product of butadiene polymerization in anenvironment of aliphatic hydrocarbons in the presence of a catalytic system based on neodymium compounds.
| Packaging | Plastic container |
| Mooney viscosity | 60-70 |
| Technical specification DS | TS 20.17.10-100-05766801-2021 |
| Shelf life | 2 year |
3. Synthetic Polybutadiene Rubber BR-1203 Ti
Introducing Synthetic polybutadiene rubber BR-1203 Ti – a premium grade synthetic rubber produced with titanium as a catalyst, offering exceptional wear resistance, low rolling resistance, and excellent adhesion properties. Ideal for tire treads, conveyor belts, and industrial applications requiring high traction and durability. Experience superior performance with BR-1203 Ti.
| Properties | Conditions | Method | Typical values* | Units |
| Mooney viscosity UML | 100 C | ASTM D 1646 | 45 ± 4 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.3 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 8.5 | MPa | |
| Tensile strength | ASTM D 412 | 11.0 | MPa | |
| Ultimate elongation | ASTM D 412 | 360 | % | |
| Minimum torque | ML | ASTM D 5289 | 2.7–3.7 | dNm |
| Maximum torque | MH | ASTM D 5289 | 16.0-20.0 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.8-3.2 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 4.5-8.0 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 8.0-12.0 | min |
| Shelf life | 2 | Year | ||
| *Typical values; not for specification. | ||||
4. Synthetic Butadiene Rubber BR-1243 E-Pro, Metal Container 1.26 & Plastic Container 0.54
Introducing Synthetic butadiene rubber BR-1243 E-Pro – a high-grade synthetic rubber produced through advanced techniques, offering excellent elasticity, low heat build-up, and enhanced processability. Perfect for applications such as automotive parts, footwear, and industrial goods that require superior performance and ease of processing. Choose BR-1243 E-Pro for reliable quality and optimal results.
| Properties | Conditions | Method | Typical values* | Units |
| Mooney viscosity UML | 100 C | ASTM D 1646 | 44 ± 5 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.7 | % | |
| Shelf life | 1 | Year |
5. Synthetic Polybutadiene Rubber BR-1243 Nd
Introducing Synthetic polybutadiene rubber BR-1243 Nd – a high-quality synthetic rubber produced with neodymium as a catalyst, offering excellent abrasion resistance, low hysteresis, and superior tear strength. Perfect for applications such as tires, conveyor belts, and various industrial products that require exceptional durability and performance. Trust BR-1243 Nd for reliable and long-lasting results.
| Properties | Conditions | Method | Typical values* | Units |
| Mooney viscosity UML | 100 C | ASTM D 1646 | 44 ± 5 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Antioxidant | СAS110553-27 | 0,2–0,4 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 11.0 | MPa | |
| Tensile strength | ASTM D 412 | 16.8 | MPa | |
| Ultimate elongation | ASTM D 412 | 360 | % | |
| Minimum torque | ML | ASTM D 5289 | 2.0–3.8 | dNm |
| Maximum torque | MH | ASTM D 5289 | 15.4-22.0 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 2.3-4.5 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 5.5-8.5 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 9.0-13.0 | min |
| Shelf life | 2 | Year | ||
| *Typical values; not for specification. | ||||
ACRYLONITRILE-BUTADIENE RUBBER (NBR)
Introducing Acrylonitrile-butadiene rubber (NBR) – a premium synthetic rubber produced through the copolymerization of acrylonitrile and butadiene, known for its excellent oil and fuel resistance, durability, and flexibility. Widely used in automotive seals, gaskets, hoses, and various industrial applications requiring oil and chemical resistance. Experience the reliability and performance of NBR for your specific needs.
1. Acrylonitrile-Butadiene Rubber Power (PNBR)
Introducing Acrylonitrile-butadiene rubber powder (PNBR) – a finely ground form of synthetic rubber produced through a specialized milling process, offering excellent dispersibility and enhanced blending capabilities. Ideal for applications such as adhesives, coatings, and sealants where high performance and improved processing are essential. Experience the convenience and versatility of PNBR for your specific formulation needs.
| Parameter | Test method | PNBR3345 | PNBR3355 | PNBR3365 |
| Mooney viscosity MML 1+4 (100 °C) raw rubber before grinding | ASTM D 1646 | 40-49 | 50-60 | 61-70 |
| Acrylonitrile content (initial polymer) rawrubber before grinding , % | Method ofsupplier | 31-35 | 31-35 | 31-35 |
| Volatile matter content, wt % | ASTM D 5668 | ≤ 0,8 | ≤ 0,8 | ≤ 0,8 |
| Antiaglomerate PVC, % | Method of supplier | 06-12 | 06-12 | 06-12 |
| The size of particles is less than 1,0 mm % | Method of supplier | ≥ 99 | ≥ 99 | ≥ 99 |
| Antioxidant type | non staining | |||
2. Synthetic Acrylonitrile-Butadiene Rubber NBR
Introducing Synthetic acrylonitrile-butadiene rubber (NBR) – a top-grade synthetic rubber produced through the copolymerization of acrylonitrile and butadiene, known for its exceptional oil, fuel, and chemical resistance. Widely used in automotive, industrial, and sealing applications where durability and resilience are vital. Trust NBR for reliable performance in demanding environments.
2.1 Acrylonitrile-butadiene rubber NBR 1865 plywood container 1.26 & cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Acrylonitrile content | method ofsupplier | 17–20 | % | |
| Mooney viscosity UML | 100 C | ASTM D 1646 | 62-68 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 6.9 | MPa | |
| Tensile strength | ASTM D 412 | 17.6 | MPa | |
| Ultimate elongation | ASTM D 412 | 400 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.3–2.9 | dNm |
| Maximum torque | MH | ASTM D 5289 | 10.8-14.6 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 2.2-5.0 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.3-6.1 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 6.7-10.1 | min |
| Shelf life | 1.5 | Year | ||
| *Typical values; not for specification. | ||||
2.2 Acrylonitrile-butadiene rubber NBR 1855 plywood container 1.26
| Properties | Conditions | Method | Typicalvalues* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 55±3 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 17–20 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 6.9 | MPa | |
| Tensile strength | ASTM D 412 | 17.6 | MPa | |
| Ultimate elongation | ASTM D 412 | 400 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.9±0.8 | dNm |
| Maximum torque | MH | ASTM D 5289 | 11.9±1.8 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 3.6±1.4 | Min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 4.7±1.4 | Min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 8.4±1.7 | Min |
| Shelf life | 1 | Year | ||
| *Typical values; not for specification. | ||||
2.3 Acrylonitrile-butadiene rubber NBR 3335 plywood container 1.26 & cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 32-38 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 31-35 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 8.8 | MPa | |
| Tensile strength | ASTM D 412 | 22.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 0.6-1.6 | dNm |
| Maximum torque | MH | ASTM D 5289 | 11.3-15.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.9-4.3 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.6-6.8 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 13.2-19.8 | min |
| Shelf life | 1.5 | Year | ||
| *Typical values; not for specification. | ||||
2.4 Acrylonitrile-butadiene rubber NBR2655 plywood container 1.26 & cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 32-38 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 31-35 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 8.8 | MPa | |
| Tensile strength | ASTM D 412 | 22.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 0.6-1.6 | dNm |
| Maximum torque | MH | ASTM D 5289 | 11.3-15.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.9-4.3 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.6-6.8 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 13.2-19.8 | min |
| Shelf life | 1.5 | Year | ||
| *Typical values; not for specification. | ||||
2.5 Acrylonitrile-butadiene rubber (fast curing) NBR 2675 FC cardboard container 0.54 & plywood 1.26
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 52-58 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 27-30 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 8.8 | MPa | |
| Tensile strength | ASTM D 412 | 22.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.0-2.4 | dNm |
| Maximum torque | MH | ASTM D 5289 | 12.2-16.6 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.9-4.5 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.2-6.0 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 10.6-16.0 | min |
| Shelf life | 1.5 | Year | ||
| *Typical values; not for specification. | ||||
2.6 Acrylonitrile-butadiene rubber NBR 3380 NT plywood container 1.08
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 72-78 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 27-30 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 9.8 | MPa | |
| Tensile strength | ASTM D 412 | 23.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.3-2.9 | dNm |
| Maximum torque | MH | ASTM D 5289 | 16.7-21.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.7-4.1 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.0-5.6 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 6.1-10.9 | min |
| Shelf life | 1 | Year | ||
| *Typical values; not for specification. | ||||
3.Solution Styrene-Butadiene Rubber (SSBR)
Introducing Solution styrene-butadiene rubber (SSBR) – a premium synthetic rubber produced through solution polymerization, offering excellent processability, high elasticity, and low rolling resistance. Ideal for tire manufacturing, footwear, and various industrial applications requiring superior performance and fuel efficiency. Choose SSBR for exceptional quality and reliability.
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 50 ± 4 | UM |
| 1,2 units,% | ISO 21561 | 61.0-67.0 | % | |
| Bound styrene | ISO 21561 | 25.0 ± 1.0 | % | |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Solvent extract | method of supplier | 26.3-29.3 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 8.8 | MPa | |
| Tensile strength | ASTM D 412 | 15.0 | MPa | |
| Ultimate elongation | ASTM D 412 | 350 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.6-3.3 | dNm |
| Maximum torque | MH | ASTM D 5289 | 10.0-18.0 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 3.6-7.0 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 6.7-10.5 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 12.2-20.3 | min |
| Shelf life | 2 | Year | ||
| *Typical values; not for specification. | ||||
4.Emulsion Styrene-Butadiene Rubber With Oil (SBR)
Introducing Emulsion styrene-butadiene rubber with oil (SBR) – a high-quality synthetic rubber produced through emulsion polymerization with added oil, providing enhanced processability, flexibility, and improved wear resistance. Widely used in tire treads, conveyor belts, and various industrial applications requiring durability and versatility. Trust SBR for reliable performance in demanding environments.
4.1 Styrene-butadiene rubber SBR-1723 TDAE B metal and plywood 1.26 & plastic and cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 72-78 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 27-30 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 9.8 | MPa | |
| Tensile strength | ASTM D 412 | 23.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.3-2.9 | dNm |
| Maximum torque | MH | ASTM D 5289 | 16.7-21.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.7-4.1 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.0-5.6 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 6.1-10.9 | min |
| Shelf life | 1 | Year | ||
| *Typical values; not for specification. | ||||
4.2 Styrene-butadiene rubber SBR-1705 HI-AR B metal or plywood 1.26 & cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 72-78 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 27-30 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 9.8 | MPa | |
| Tensile strength | ASTM D 412 | 23.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.3-2.9 | dNm |
| Maximum torque | MH | ASTM D 5289 | 16.7-21.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.7-4.1 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.0-5.6 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 6.1-10.9 | min |
| Shelf life | 1 | Year | ||
| *Typical values; not for specification. | ||||
4.3 Rubber SBR-1712 B cardboard 0.54
| Properties | Conditions | Method | Typical values* | Units |
|---|---|---|---|---|
| Mooney viscosity UML | 100 C | ASTM D 1646 | 72-78 | UM |
| Volatile matter | ASTM D 5668 | 0.8 | % | |
| Ash | ASTM D 5667 | 0.5 | % | |
| Acrylonitrile content | method of supplier | 27-30 | % | |
| Tensile stress at 300 % elongation | ASTM D 412 | 9.8 | MPa | |
| Tensile strength | ASTM D 412 | 23.5 | MPa | |
| Ultimate elongation | ASTM D 412 | 450 | % | |
| Minimum torque | ML | ASTM D 5289 | 1.3-2.9 | dNm |
| Maximum torque | MH | ASTM D 5289 | 16.7-21.3 | dNm |
| Scorch time | ts´1 | ASTM D 5289 | 1.7-4.1 | min |
| Time to 50 % of full cure | t’50 | ASTM D 5289 | 3.0-5.6 | min |
| Time to 90 % of full cure | t’90 | ASTM D 5289 | 6.1-10.9 | min |
| Shelf life | 1 | Year | ||
| *Typical values; not for specification. | ||||
5.Emulsion Styrene-Butadiene Rubber Without Oil (SBR)
Introducing Emulsion styrene-butadiene rubber without oil (SBR) – a premium synthetic rubber produced through emulsion polymerization without added oil, offering excellent resilience, abrasion resistance, and good processability. Widely used in tire sidewalls, footwear, and various industrial applications requiring high strength and flexibility. Choose oil-free SBR for superior performance and quality.
5.1 Rubber SBR-1500
| Parameter | Test method | SBR-1500 | ||
| grade A | grade B | grade C | ||
| Mooney viscosity ML 1+4 (100 °C) | ASTM D 1646 | 46±4 | 51±5 | 53±5 |
| Organic acids content, % | ASTM D 5774 | 5.0-7.0 | 5.0-7.0 | 5.0-7.0 |
| Organic acids soap content, %, max. | ASTM D 5774 | 0.3 | 0.3 | 0.3 |
| Bound styrene content, % | Method of supplier | 23.5±1.0 | 23.5±1.0 | 23.5±1.0 |
| Volatile matter content, wt % | ASTM D 5668 | 0.8 | 0.8 | 0.8 |
| Ash content, %, max | ASTM D 5667 | 0.5 | 0.5 | 0.5 |
| Antioxidant content (CAS№68610-06-0),% | Method of supplier | 1.0-2.0 | 1.0-2.0 | 1.0-2.0 |
| Antioxidant content (Irganox 1520L), % | Method of supplier | 0.4-0.8 | 0.4-0.8 | 0.4-0.8 |
| Tensile strength at 300 % stretching, MPa, min | ASTM D 3185 | 13 | 13 | 13 |
| Tensile strength at stretching, MPa, min | ASTM D 3185 | 22.5 | 22.5 | 22.5 |
| Relative elongation at break, %, min | ASTM D 3185 | 420 | 420 | 420 |
| Minimum torque (ML), dNm | ASTM D 5289 | 1.8-3.0 | 1.8-3.0 | 1.8-3.0 |
| Maximum torque (MH), dNm | ASTM D 5289 | 15.0-21.0 | 15.0-21.0 | 15.0-21.0 |
| Prevulcanization start time (ts1), min | ASTM D 5289 | 2.2-4.5 | 2.2-4.5 | 2.2-4.5 |
| Time to 50% vulcanization (T'50), min | ASTM D 5289 | 7.0-12.0 | 7.0-12.0 | 7.0-12.0 |
| Time to 90% vulcanization (T'90), min | ASTM D 5289 | 13.0-21.0 | 13.0-21.0 | 13.0-21.0 |
| Shelf life | 1 | Year | ||
5.2 Rubber SBR-1502
| Parameter | Test method | SBR-1502 | |
| grade B | grade C | ||
| Mooney viscosity ML 1+4 (100 °C) | ASTM D 1646 | 51±5 | 53±5 |
| Organic acids content, % | ASTM D 5774 | 5.0-7.0 | 5.0-7.0 |
| Organic acids soap content, %, max. | ASTM D 5774 | 0.3 | 0.3 |
| Bound styrene content, % | Method of supplier | 23.5±1.0 | 23.5±1.0 |
| Volatile matter content, wt % | ASTM D 5668 | 0.8 | 0.8 |
| Ash content, %, max | ASTM D 5667 | 0.5 | 0.5 |
| Antioxidant content (CAS№68610-06-0),% | Method of supplier | 1.0-2.0 | 1.0-2.0 |
| Antioxidant content (Irganox 1520L), % | Method of supplier | 0.4-0.8 | 0.4-0.8 |
| Tensile strength at 300 % stretching, MPa, min | ASTM D 3185 | 13 | 13 |
| Tensile strength at stretching, MPa, min | ASTM D 3185 | 22.5 | 22.5 |
| Relative elongation at break, %, min | ASTM D 3185 | 420 | 420 |
| Minimum torque (ML), dNm | ASTM D 5289 | 1.8-3.0 | 1.8-3.0 |
| Maximum torque (MH), dNm | ASTM D 5289 | 15.0-21.0 | 15.0-21.0 |
| Prevulcanization start time (ts1), min | ASTM D 5289 | 2.2-4.5 | 2.2-4.5 |
| Time to 50% vulcanization (T'50), min | ASTM D 5289 | 7.0-12.0 | 7.0-12.0 |
| Time to 90% vulcanization (T'90), min | ASTM D 5289 | 13.0-21.0 | 13.0-21.0 |
| Shelf life (year) | 1 | 1 | |
6. Butyl Rubber (IIR)
Introducing Butyl rubber (IIR) – a superior synthetic rubber produced through copolymerization of isobutylene and a small amount of isoprene, known for its exceptional impermeability to gases and liquids. Widely used in tire inner tubes, seals, and various applications requiring excellent air and moisture resistance. Trust Butyl rubber for reliable performance and durability in demanding environments.
| Properties | Method | Typical values | Units |
|---|---|---|---|
| Mooney viscosity ML (1+8) @125 °C (unmassed) | ASTM D1646 | 46 – 56 | MU |
| Unsaturation | Method of supplier | 1.4 – 1.8 | mol % |
| Volatile Matter | ASTM D5668 | 0.3 max | wt % |
| Ash | ASTM D5667 | 0.3 max | wt % |
| Non-staining Antioxidant | Method of supplier | 0.02 – 0.08 | wt % |
| Calcium Stearate | Method of supplier | 1.2 max. | wt % |
| Shelf life | 2 | year |
Location
Address: P2-ELOB Office No. E2-119G- 30
Hamriyah Free Zone
Sharjah
United Arab Emirates
Email: info@azkaglobal.com
Phone: 971 505097988
Schedule your visit
Working Hours:
8:00 AM – 6:00 PM
Get in touch
To learn more about the technical specifications and pricing of our gasoil products, please fill out our contact form and one of our product experts will be in touch shortly.